PENGARUH FRAKSI VOLUME PENGUAT TERHADAP KEKUATAN LENTUR GREEN COMPOSITE UNTUK APLIKASI PADA BODI KENDARAAN

http://doi.org/10.22216/jit.2015.v9i4.409


Mastariyanto Perdana(1*)

(1) Institut Teknologi Padang
(*) Corresponding Author

Abstract


Composites are one of material be used in engineering field. This is due the composites has light weight and relatively strong properties. The synthesis fiber-based composites reduces to obtain environmental friendly properties. This research use hybrid fiber which consist of calcium carbonate (CaCO3) powder and bagasse fiber. Matrix used is resin polyester. Variation of volume fraction between bagasse and calcium carbonate powder are 10:20, 15:15 and 20:10 respectively. Volume fraction of hybrid fiber and polyester is 30:70. This study aims to determine mechanical properties of hybrid composites for each variation of volume fraction. Test results showed. Bending strength of bagasse-based hybrid composites and powder of calcium carbonate with a variation of volume fraction of 10%: 20%, 15%: 15% and 20%: 10% are 53.77 MPa, 54.90 MPa and 59.76 MPa. Hybrid composites with volume fraction 20% bagasse and 10% calcium carbonate powder has highest of bending strength. Green composite based bagasse and calcium carbonate powder can use on application of vehicle body.


Komposit merupakan salah satu material yang banyak digunakan pada bidang keteknikan. Ini dikarenakan komposit memiliki sifat ringan dan relatif kuat. Untuk mendapakatkan sifat yang ramah lingkungan, penggunaan komposit yang berbasis serat sintesis dikurangi penggunaannya. Penelitian ini menggunakan serat hibrid yaitu penggabungan antara serbuk kalsium karbonat (CaCO3) dan serat ampas tebu (bagasse). Matrix yang digunakan adalah resin polyester.Variasi fraksi volume antara bagasse dan serbuk kalsium karbonat masing-masing adalah 10:20, 15:15 dan 20:10. Fraksi volume antara serat hibrid dan resin polyester adalah 30:70. Penelitian ini bertujuan untuk mengetahui sifat mekanik dari komposit hibrid berbasis bagasse dan serbuk kalsium karbonat untuk masing-masing variasi fraksi volume. Hasil pengujian menunjukkan bahwakekuatan bending tertinggi komposit hibrid berbasis bagasse dan serbuk kalsium karbonat adalah fraksi volumeserat 20% bagasse dan 10% serbuk kalsium karbonat yang mempunyai kekuatan bending sebesar 59.76 MPa. Kekuatan bending dari komposit hibrid berbasis bagasse dan serbuk kalsium karbonatdengan variasi fraksi volume 10% : 20%, 15% : 15% dan 20% : 10% adalah 53.77 MPa, 54.90 MPa dan 59.76 MPa.Komposit ramah lingkungan berbasis serat ampas tebu dan serbuk kaslium karbonat dapat diaplikasikan pada bodi kendaraan


Keywords


bagasse; bending strength; calcium carbonate; hybrid composite; volume fraction

Full Text:

PDF

References


Anonim, 2004. Annual Book ASTM Standard Volume 8 790. USA

Balaji, A., Karthikeyan, B., and Sundar, R., 2014. Bagasse Fiber – The Future Biocomposite Material: A Review. International Journal of Cemtech Research. 7 (1). 223 – 233

Daud, J., J., A., Anindito, P., dan Yudi, S., I., 2012. Pengaruh Fraksi Volume Serat Pelepah Gebang (Corypha Utan Lamarck) Terhadap Sifat Mekanik Pada Komposit Bermatriks Epoxy. Jurnal Rekayasa Mesin, Vol. 3, No. 2. 352 – 361.

Heru, P., S., Suhardoko, dan Bambang, T., B., 2015. Pengaruh Fraksi Volume dan Panjang Serat Terhadap Sifat Bending Komposit Polyester yang diperkuat Serat Limbah Batang Pisang. Prosiding SNST. 92 – 96.

Huda, M.S., Mohanty, A.K., Drzal, L.T., Schut, E., and Misra, M., 2005. Green Composite From Recycled Cellulose and Poly (lactid-acid) : Physico-mechanical and Morphological Proprties Evaluation. Journal Material Science. 40(16) : 4221-4229

Jones R M, 1999. Mechanics of Composite Materials. Second Edition. Taylor & Francis. USA

Laga, S., S., dan Moh, F., 2015. Pengaruh Panjang Serat Terhadap Nilai Koefisien Absorpsi Suara dan Sifat Mekanik Komposit Serat Ampas Tebu dengan Matrik Gipsum. Jurnal Teknik ITS. Vol. 4, No. 1. 101-105.

Laula, N., dan Adhi, N., 2014. Pemanfaatan Limbah Ampas Tebu Melalui Desain Produk Perlengkapan Rumah . Jurnal Tingkat Sarjana Seni Rupa dan Sains. 1(1). 1 - 7

Luz, S., M., Goncalves, A.R., and Del, A., Jr. 2007. Mechanical Behavior and Microstructural Analysis of Sugar Cane Bagasse Fiber Reinforced Polypropylene Composite. Journal Composite. Part A-Applied and Manufacturing. Elsevier. Vol 38(6). 1455-1461

Nadji, A., S., Rizky S., R., dan Muhammad H., 2014. Pengaruh Rasio Epoksi/Ampas Tebu dan Perlakuan Alkali pada Ampas Tebu Terhadap Kekuatan Bentur Komposit Partikel Epoksi Berpengisi Serat Ampas Tebu. Jurnal Teknik Kimia USU. 3(3). 28 – 31

Ning, Liu., et al., 2015. Effect of Nano-sized and Micro-sized Carbon Fiber on Interlaminar Shear Strength and Tribological Properties of High Strength Glass Fabric/Penolic Laminate in Water Environment. Journal of Composite ; Part B. Elsevier. No. 68, 92 – 99

Nurhidayat, A., dan Wijoyo, 2014. Pengaruh Fraksi Volume Serat Cantula Terhadap Ketangguhan Impak Komposit Cantula – HDPE Daur Ulang Sebagai Bahan Core Lantai Ramah Lingkungan. Prosiding Seminar Nasional Teknologi dan Informatika (SNATIF) - 1. Universitas Muria Kudus. 145 – 152.

Oluwole, I., O., 2014. Effect of Bagasse Fiber Reinforcement on the Mechanical Properties of Polyester Composites. The Journal of the Association of Professional Engineers of Trinidad and Tobago. 42(1). 12 – 15

Perdana, M., dan Jamasri, 2015. Fracture Surface Komposit Hibrid Berbasis Fiberglass Dan Coir Akibat Pengaruh Thermal Cyclic. Seminar Nasional Peran Iptek Menuju Insdustri Masa Depan - 3 (PIMIMD - 3). Institut Teknologi Padang.

Putra, H., 2011. Pengaruh Larutan Natrium Hidroksida pada Serat Eceng Gondok Terhadap Sifat Mekanik. Skripsi. Jurusan Teknik Mesin. Universitas Andalas. Padang

Rahman, M., M., and Mubarak A., K., 2007. Surface treatment of coir (Cocos nucifera) fibers and its influence on the fibers’ physico-mechanical properties. Journal of Composites Science and Technology 67. 2369-2376

Ramli, R., et.al. 2013. Developmet of Cu Nanoparticle Loaded Oil Palm Fiber Reinforced Nanocomposite. Journal of Advance in Nanoparticle. Vol. 2, 358-365.

Siswanto dan Kuncoro, D., 2011. Pengaruh Fraksi Volume dan Ukuran Partikel Komposit PolyesterResin BerpenguatPartikel Genting Terhadap Kekuatan Tarik dan Kekuatan Bending. Jurnal Politeknosains. Vol. X, No. 2, 91 – 99

Verma, D., et al. 2012. Bagasse Fiber Composite – A Review. Journal Material Environment and Science 3(6) 1079 – 1092.

Yeremias, M., P., 2012. Pengaruh Fraksi Volume Terhadap Karakterisasi Mekanik Green Komposit Widuri – Epoxy. Seminar Nasional Sains dan Teknik. 114 – 120.

Yoweri, W., G., Perdinan, S., dan M., Syukur., 2013. Pembuatan dan Karakterisasi Komposit Serat Palem Saray dengan Matrik Epoxy. Jurnal Saintika Fisika. Vol. 1, No. 1


Refbacks

  • There are currently no refbacks.


Copyright (c) 2016 Jurnal Ipteks Terapan

Online ISSN : 2460-5611 | Print ISSN : 1979-9292

Publish by LLDIKTI Wilayah X (Sumatera Barat, Riau, Jambi dan Kepulauan Riau)

Jl. Khatib Sulaiman No 1 Kota Padang. Kode Pos 25144. Telp 0751-7056737. Fax 0751-7056737. Website:http://www.kopertis10.or.id

Web Analytics Made Easy - StatCounter View My Stats

Creative Commons License 

This work is licensed under a Creative Commons Attribution 4.0 International License.